NewPro Grasp Protection for Metal Surfaces Suitable for Clinics / Nursing Home
Product description
The grasp protection for Metal Surfaces is suitable for highgrade Stainless steel, chrome, aluminium, brass, copper and other metals. The coating material protects unpolished and shining metal surfaces durably against annealing colors and finger marks. It increases the surface smoothness, reduces the contamination and facilitates cleaning. By a durable connection to the substate the surface possesses a high mechanical and chemical ruggedness.
Consumption: Approx. 15 g/m² (wiped/rolled), approx. 25 g/m² (painted)
Drying process and hardening: Ambient temperature
Application: Polishing, dipping
Gross density: 0, 839 kg / liter
Main areas of application
Brushed and Matted Surfaces Made of Stainless Steel, Chrome, Aluminium, Brass, Copper and other Metals.
Material basis:
- Solvent-Based Polymer Matrix.
Color:
- Colorless, Transparent
PH-Values:
- > 7, basic
Packaging Sizes:
- 1-L-PE Bottle 0. 8 kg
- 5-L-PE Canister 3. 6 kg.
- 20-L-PE Canister 16. 0 kg
- 200-L-PE- Barrel 168. 0 kg
Storage:
Minimum of 6 months at a temperature from 5 degrees Celsius to 35 degrees Celsius when stored in tightly sealed original container. Protect against frost and higher temperatures. In the event of storage beyond expiration date, test the material prior to use. Tightly air seal opened containers to preserve product life. Ensure sufficient ventilation in product storage areas.
Preparation: No preparation necessary – Material comes ready for use and application directly from the package.
Application
Application: Apply according to separate instructions for use.
Apply product at air and object surface temperatures from 5 degrees Celsius to 35 degrees Celsius. Product dries within a maximum of 24 hours at room temperature, or in 1 hour at 160 Degrees Celsius. Variations from these external conditions could influence the hardening time. Use and Application: Approximate use of the product: 15 g/m2 (wiped or rolled), approximately 25 g/m2 (brushed).
Safety and Protective Measures
During application and use, carefully follow the instructions and safety precautions on the package label, as well as the pertinent safety and accident instructions of appropriate occupational and trade associations. For further detailed instructions, see safety data sheets.
Cleaning of tools
- Clean tools using alcohol or soak in lime potash.
Improvements and Second Coatings:
Remove with standard lacquer remover or mechanically using abrasive finishing.
Cleaning of Coated Surfaces
subsequent to hardening, follow usual trade practices using common mild household cleaners.
Disposal of Waste /Remains
Dispose of material residues according to local and/or state regulation for paints and lacquers.
Technical Data
Salt Spray: (DIN EN ISO 9227 NSS): 240h (Aluminum), 500h (stainless steel)
Weathering: (DIN EN ISO 4892-3: 4h UV-B 60°C: 4h water condensation 50°C): 240h
Climate change: DBL 7906; 15 min 23° C; 4 h - 30°C: 30 cycles 15 min 23°C, 4h 80° C: 30 min 40°C 98% rel. humidity
Acid/Base Resistance: pH 2 to pH 10
Pencil Hardness: 5H (stainless steel), 4H (aluminum)
Tabertest: 5 mg(CS 10 F roll: 1000 tests): Temperature resistant: continuous up to 200°C –
Surface Energy: 24 MN/m