High-temperature resistance corrosion protection for light metals
Product is replaced with NewPro NanoDuration NC or NewPro Long Term Coating RK CCS. Please check if product is suitable for the intended purpose.
Product Description
The coating material produces a mechanically resistant coating with a high asset liability on light metals. The surface system generates matte coating with good abrasion resistance, and good resistance to high temperatures (up to 450C) and corrosive media, such as acidic and alkaline condensates. The surface does not need chromate coating. Product is chromate and lead free in terms of the hazardous substances ordinance. Consumption depends on surface coarseness and application method.
Main areas of application
Material Basis:
- Inorganic-Organic 2-K Hybrid System, Solvent-Based
Color:
- Hardened beige-matt
PH-Values:
- < 7, light acid
Package Sizes:
- 5-L-PE Canister 5 kg.
- Further package/container sizes available upon request
Storage
Minimum of 6 months at a temperature from 5 degrees Celsius to 20 degrees Celsius when stored in tightly sealed original container. Protect against frost and higher temperatures. In the event of storage beyond expiration date, test the material prior to use. Tightly air seal opened containers to preserve product life. Ensure sufficient ventilation in product storage areas.
Preparation
Mix lacquer thoroughly before usage. For larger baths we suggest liquor circulation. Subsequent dipping possible for thicker coatings.
Application temperatures: Air and object temperature 5°C to 35°C. Different environemtal conditions can influence hardening time. Burning-in coating at 200°C for 1 hour.
Consumption: Consumption depends on surface coarseness and application method.
Protective Measures
During application and use, carefully follow the instructions, safety advice and the pertinent safety and accident instructions of appropriate occupational and trade associations. For further detailed instructions, see safety data sheets. Cleaning of Tools:
- Clean tools thoroughly with thinner and towel.
Improvement and Second Coatings:
- Mechanically through abrasive finishing (ie., sandpaper) or through emplacement in a bath of lime potash and 2-Propanol.
Disposal:
- Dispose of material residues according to local and/or state regulation for paints and lacquers.
Technical Data
Salt Spray (DIN EN ISO 9227 NSS): 100hCASS (DIN EN ISO 9227 CASS): 72h
Weathering (DIN EN ISO 4892-3: 4h UV-B 60°C; 500h4h water condensation 50°C)
Climate change DBL 7906; 15 min 23° C; 4h-30°C: 5 cycles15 min 23^c; 4h 80°C; 30 min 40°C 98% re. humidity.
Acis / Base Resistance: pH 1 to pH 11
Pencil Hardness: HB
Taber test (CS 10 roll): 1000 rotations: 96 mg
Temperature resistance: continuous at 450°C